0.3mm Diameter S110 Low Carbon Steel Shot for Shot Blasting Auto Parts Shotblast Type
Product Details:
| Place of Origin: | China |
| Certification: | ISO 9001, ISO 9000, ISO 14001, ISO 14000, ISO 20000, HSE, QC 080000, BSCI |
Payment & Shipping Terms:
| Minimum Order Quantity: | 1 set |
|---|---|
| Price: | Negotiable |
| Delivery Time: | Peak Season Lead Time: 1-3 months Off Season Lead Time: 1-3 months |
| Payment Terms: | LC, T/T, D/P, PayPal, Western Union, Small-amount payment |
| Supply Ability: | 500 Sets Per Years |
|
Detail Information |
|||
| Model NO.: | S110 | Shotblast Application: | Auto Parts |
|---|---|---|---|
| Sandblasting Method: | Dry Spray | Sandblasting Applications: | Metallurgy |
| Transport Package: | Bags | Specification: | 25kg*40bags |
| Trademark: | Pumingwwei | Origin: | China |
| HS Code: | 72051000 | Supply Ability: | 60000tons |
| Customization: | Available | Shotblast Type: | Shot Blasting |
| Shotblast Material: | Steel Shot | ||
Product Description
Eliminating The Welding Stress Cast Steel Shot Used for Machinery Cleaning
S 110 Low Carbon Steel Shot with Shot Blasting Machine
S110 steel shot refers to a steel shot with a product diameter of 0.3mm. S110 can achieve good coverage in a short time. For various castings with high requirements on the surface of the workpiece, the s110 steel shot has uniform hardness and good cleaning effect. ,Durable wear.
| Application: | Abrasive Refractory Industry |
|---|---|
| Function: | Descaling |
| Particle Size: | Customer Requirement |
| Hardness: | Superabrasive |
| Density: | ≥7g/cm3 |
| Microstructure: | Homogeneous Tempered Martensite or Troostite |
Low Carbon Steel Shot
Low Hardness Extreme Durability Round Shape Safe on Delicate and Sensitive Parts Works in Standard Blast Equipment Little to No Dusting Won't Damage Part Details No Work Hardening of the Part Resists Breaking Down No Metal Removal from Part Surface Applications Deburring Delicate Machined Parts and Stampings Cleaning Investment Castings Remove Release Agent Build-up on Molds Corrosion Removal Remove Heat Treat Scale Deflashing Die Cast Aluminum Parts
Hight Carbon Steel Shot
Is used in wheel blasting equipment. It also gives a hammered or peened effect for use on ferrous castings and fabrication Our High-carbon steel shot is a very powerful abrasive for the surface treatment of metallic products. In contrast to low carbon steel shot round, this product has a higher beam intensity and thus enables faster working. Steel shot also has a use in the removal of scale, rust and surface contaminant and used foundries for de-burring or de-flashing of castings and cleaning moulds.
| mesh | mm | Specifications of steel shot | ||||||||||
| SS-2.5 | SS-2.0 | SS-1.7 | SS-1.4 | SS-1.2 | SS-1.0 | SS-0.8 | SS-0.6 | SS-0.5 | SS-0.3 | SS-0.2 | ||
| 7 | 2.80 | All pass | ||||||||||
| 8 | 2.36 | All pass | ||||||||||
| 10 | 2.00 | 85%min | All pass | All pass | ||||||||
| 12 | 1.70 | 97%min | 85%min | 5%max | All pass | |||||||
| 14 | 1.40 | 97%min | 85%min | 5%max | All pass | |||||||
| 16 | 1.18 | 97%min | 85%min | 5%max | All pass | |||||||
| 18 | 1.00 | 96%min | 85%min | 5%max | All pass | |||||||
| 20 | 0.850 | 96%min | 85%min | 10%max | All pass | |||||||
| 25 | 0.710 | 96%min | 85%min | 10%max | ||||||||
| 30 | 0.600 | 96%min | 85%min | All pass | ||||||||
| 35 | 0.500 | 97%min | 10%max | |||||||||
| 40 | 0.425 | 85%min | All pass | |||||||||
| 45 | 0.355 | 97%min | 10%max | |||||||||
| 50 | 0.300 | 80%min | ||||||||||
| 80 | 0.180 | 90%min | 80%min | |||||||||
| 120 | 0.125 | 90%min | ||||||||||
| 200 | 0.075 | |||||||||||
| 325 | 0.045 | |||||||||||
| SAE J444 | S-780 | S-660 | S-550 | S-460 | S-390 | S-330 | S-280 | S-230 | S-170 | S-110 | S-70 | |
| Name | Cast steel shot | Cast steel grit | Steel cut wire shot | Conditional cut wire shot | HQ cast steel shot | |
| Chemical composition | C | 0.80-1.20% | 0.45-0.85% | 0.45-0.85% | 0.80-1.20% | |
| Mn | 0.35-1.20% | 0.30-1.30% | 0.30-1.30% | 0.35-1.20% | ||
| Si | ≥0.40 | 0.15-0.35% | 0.15-0.35% | ≥0.40 | ||
| S | ≤0.05% | ≤0.05% | ≤0.05% | ≤0.05% | ||
| P | ≤0.05% | ≤0.04% | ≤0.04% | ≤0.05% | ||
| hardness | Routine:40-50HRC | GP steel grit 42-52HRC | 1.0mm:42-53HRC | 45-60HRC | Routine:42-47HRC Special:52-56HRC Special:56-60HRC | |
| Special:52-56HRC | GP steel grit 53-60HRC | 1.5mm:41-45HRC | ||||
| Special:56-60HRC | GP steel grit 60-64HRC | |||||
| Hardness deviation | The max deviation range:±3.0HRC | |||||
| Tensile intensity | - | 1300-2200Mpa | 2200-2800Mpa | - | ||
| Durability | 2000-28000 times | 3300-4000times | 4000times | 2800-3300times | ||
| Microstructure | Tempered martensite or sorbite | Deformed pearlite | Deformed sorbite | Tempered martensite or sorbite | ||
| Density | 7.4g/cm3 | 7.6g/cm3 | 7.8g/cm3 | 7.8g/cm3 | 7.4g/cm3 | |
| Bulk density | 4.4g/cm3 | 4.2g/cm3 | 4.5g/cm3 | 4.5g/cm3 | 4.4g/cm3 | |